سیمان پرتلند تیپ دو - 325 - شرکت سیمان نهاوند

محصولات

Remarks	Result	Range of ASTM	Method	Unit	Unit	Test Parameters	No
	1.80	Max 3.0	ASTM C-114	%	LOI	Loss on Ignition	1
	21.10		ASTM C-114	%	SiO2	Silicon Dioxide	2
	4.80	Max 6.0	ASTM C-114	%	Al2O3	Aluminium Oxide	3
	3.90	Max 6.0	ASTM C-114	%	Fe2O3	Ferric Oxide	4
	63.0	-	ASTM C-114	%	CaO	Calcium Oxide	5
	1.85	Max 6.0	ASTM C-114	%	MgO	Magnesium Oxide	6
	2.54	Max 3.0	ASTM C-114	%	SO3	Sulfur Trioxide	7
	0.33	-	ASTM C-114	%	Na2O	Sodium Oxide	8
	0.86	-	ASTM C-114	%	K2O	Potassium Oxide	9
	0.38	Max 1.5	ASTM C-114	%	IR	Insoluble Residue	10
	51.0	-	Bouge Method	%	C3S	Tricalcium Silicate	11
	21.9	-	Bouge Method	%	C2S	Dicalcium Silicate	12
	6.1	Max 8.0	Bouge Method	%	C3A	Tricalcium Aluminate	13
	11.9	-	Bouge Method	%	C4AF	Calcium Alumino Ferrite	14
Max 3600	3200	Min 2600	ASTM C-204	Cm2/gr		Fineness Blaine	15
	10.0%			45µ		Fineness Sieve	16
	0.2			90µ		Fineness Sieve	17
	26	-	ASTM C-178	%		Water for Normal Consistency	18
	-	-	ASTM C-191			Setting Time - Vicat Test	19
	140	Min 45	ASTM C-191	Min		Initinal	20
	375	Max 6.0	ASTM C-191	Min		Final	21
	190	-	ASTM C-109	kg/cm2	2days	Compressive Strength	22
	230		ASTM C-109	kg/cm2	3days	Compressive Strength	23
	310	Min 200	ASTM C-109	kg/cm2	7days	Compressive Strength	24
	400	Min 325	ASTM C-109	kg/cm2	28days	Compressive Strength	25
	0.07	Max 0.8	ASTM C-151	%		Autoclave Expansion	26

Quality Control .Lab ISO/IEC 17025:2005

Interpretation Sample:

Lab Manager: F.Aboulghazi

Factory Manager: H.Sabzali

NCOCL-FO48-R02

سیمان پرتلند

سفارش

MSDS

برگه اطلاعات ایمنی مواد

Result	Range of ASTM	Method	Unit	Test Parameters
1.80	Max 3.0	ASTM C-114	LOI%	Loss on Ignition
21.10		ASTM C-114	SiO2%	Silicon Dioxide
4.80	Max 6.0	ASTM C-114	Al2O3%	Aluminium Oxide
3.90	Max 6.0	ASTM C-114	Fe2O3%	Ferric Oxide
63.0	-	ASTM C-114	CaO%	Calcium Oxide
1.85	Max 6.0	ASTM C-114	MgO%	Magnesium Oxide
2.54	Max 3.0	ASTM C-114	SO3%	Sulfur Trioxide
0.33	-	ASTM C-114	Na2O%	Sodium Oxide
0.86	-	ASTM C-114	K2O%	Potassium Oxide
0.38	Max 1.5	ASTM C-114	IR%	Insoluble Residue
51.0	-	Bouge Method	C3S%	Tricalcium Silicate
21.9	-	Bouge Method	C2S%	Dicalcium Silicate
6.1	Max 8.0	Bouge Method	C3A%	Tricalcium Aluminate
11.9	-	Bouge Method	C4AF%	Calcium Alumino Ferrite
3200	Min 2600	ASTM C-204	Cm2/gr	Fineness Blaine
10.0%			45µ	Fineness Sieve
0.2			90µ	Fineness Sieve
26	-	ASTM C-178	%	Water for Normal Consistency
-	-	ASTM C-191		Setting Time - Vicat Test
140	Min 45	ASTM C-191	Min	Initinal
375	Max 6.0	ASTM C-191	Min	Final
190	-	ASTM C-109	kg/cm2-2days	Compressive Strength
230		ASTM C-109	kg/cm2-3days	Compressive Strength
310	Min 200	ASTM C-109	kg/cm2-7days	Compressive Strength
400	Min 325	ASTM C-109	kg/cm2-28days	Compressive Strength
0.07	Max 0.8	ASTM C-151	%	Autoclave Expansion

Quality Control .Lab ISO/IEC 17025:2005

Interpretation Sample:

Lab Manager: F.Aboulghazi

Factory Manager: H.Sabzali

NCOCL-FO48-R02

سیمان پرتلند

سفارش

MSDS

برگه اطلاعات ایمنی مواد

سیمان پرتلند تیپ یک – 325

سیمان پرتلند تیپ یک – 425

سیمان پرتلند تیپ دو – 425

سیمان تیپ پنج – 325

سیمان پرتلند پوزولانی